It is obtained from acrylic homopolymer fibres, and becomes fibrillated after grinding. It has good reinforcement features. At low temperatures, it provides dimensional stability (after preforming). During its decomposition (at approximately 220 °C), the carbon contents increase. Basically, polyacrylonitrile fibres are used as precursors for carbon fibre.